Low-cost zeolitic rocks are promising substitutes for feldspathic fluxes in ceramic bodies, since their fusibility, modest hardness and high cation exchange capacity (CEC) should improve grinding and sintering. Five large-scale Italian deposits of natural zeolites with different mineralogy were characterised and tested in porcelain stoneware bodies. Their behaviour during processing was appraised and compared with that of zeolite-free bodies. Zeolites increased the slip viscosity during wet grinding, causing a coarser grain size distribution and consequently some drawbacks in both unfired and fired tiles. After overcoming this hindrance by dry grinding of zeolite rocks, the technological behaviour of zeolite-bearing tiles appear to be similar to that of current porcelain stoneware, though with larger firing shrinkage and residual closed porosity.
Influence of zeolites on the sintering and technological properties of porcelain stoneware tiles
LANGELLA A;
2003-01-01
Abstract
Low-cost zeolitic rocks are promising substitutes for feldspathic fluxes in ceramic bodies, since their fusibility, modest hardness and high cation exchange capacity (CEC) should improve grinding and sintering. Five large-scale Italian deposits of natural zeolites with different mineralogy were characterised and tested in porcelain stoneware bodies. Their behaviour during processing was appraised and compared with that of zeolite-free bodies. Zeolites increased the slip viscosity during wet grinding, causing a coarser grain size distribution and consequently some drawbacks in both unfired and fired tiles. After overcoming this hindrance by dry grinding of zeolite rocks, the technological behaviour of zeolite-bearing tiles appear to be similar to that of current porcelain stoneware, though with larger firing shrinkage and residual closed porosity.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.